Nonvacuum deposition of silver doped YBCO coated conductor on %100 lattice match buffered Ni tapes

L. Arda; O. Cakiroglu; S. Keskin; O. A. Sacli

doi:10.1063/1.2733508

Nonvacuum deposition of silver doped YBCO coated conductor on %100 lattice match buffered Ni tapes

L. Arda
, O. Cakiroglu
, S. Keskin
, O. A. Sacli

Araştırma çıktısı: Dergi katkısı › Konferans makalesi › Hakem

Özet

Silver doped YBa₂Cu₃O_7-δ (YBCO) coated conductors were fabricated on Gd_1.624Ho_0.376O ₃ (100% lattice match with YBCO) textured buffer layers on Ni tape by reel-to-reel sol-gel dip coating system. Sample were prepared with different wt(1-5)% Ag doped ratio. The surface morphologies and microstructure of all sample were characterized by ESEM, EDS and XRD. Pole figure texture analyses have been done to characterize texture of buffer layer and YBCO superconducting film. The critical current Ic measurement was performed using four wire method with the 1 μV/cm criterion. The critical current density, J_c was measured to be 2.2 × 10⁴ A/cm₂ at 77 K self field for 1 wt % Ag doped YBCO sample

Orijinal dil	İngilizce
Sayfa (başlangıç-bitiş)	767
Sayfa sayısı	1
Dergi	AIP Conference Proceedings
Hacim	899
DOI'lar	https://doi.org/10.1063/1.2733508
Yayın durumu	Yayınlanan - 2007
Harici olarak yayınlandı	Evet
Etkinlik	6TH International Conference of the Balkan Physical Union - Istanbul, Turkey Süre: 22 Ağu 2006 → 26 Ağu 2007

Belgeye Erişim

10.1063/1.2733508

Diger dosyalar ve linkler

Link to publication in Scopus

Bundan alıntı yap

@article{3e60781b23324347ab69e57f14fd45d3,

title = "Nonvacuum deposition of silver doped YBCO coated conductor on \%100 lattice match buffered Ni tapes",

abstract = "Silver doped YBa2Cu3O7-δ (YBCO) coated conductors were fabricated on Gd1.624Ho0.376O 3 (100\% lattice match with YBCO) textured buffer layers on Ni tape by reel-to-reel sol-gel dip coating system. Sample were prepared with different wt(1-5)\% Ag doped ratio. The surface morphologies and microstructure of all sample were characterized by ESEM, EDS and XRD. Pole figure texture analyses have been done to characterize texture of buffer layer and YBCO superconducting film. The critical current Ic measurement was performed using four wire method with the 1 μV/cm criterion. The critical current density, Jc was measured to be 2.2 × 104 A/cm2 at 77 K self field for 1 wt \% Ag doped YBCO sample",

keywords = "Ag doping, Coated conductor, Critical current, Sol-gel, YBCO",

author = "L. Arda and O. Cakiroglu and S. Keskin and Sacli, \{O. A.\}",

year = "2007",

doi = "10.1063/1.2733508",

language = "English",

volume = "899",

pages = "767",

journal = "AIP Conference Proceedings",

issn = "0094-243X",

publisher = "American Institute of Physics",

note = "6TH International Conference of the Balkan Physical Union ; Conference date: 22-08-2006 Through 26-08-2007",

}

TY - JOUR

T1 - Nonvacuum deposition of silver doped YBCO coated conductor on %100 lattice match buffered Ni tapes

AU - Arda, L.

AU - Cakiroglu, O.

AU - Keskin, S.

AU - Sacli, O. A.

PY - 2007

Y1 - 2007

N2 - Silver doped YBa2Cu3O7-δ (YBCO) coated conductors were fabricated on Gd1.624Ho0.376O 3 (100% lattice match with YBCO) textured buffer layers on Ni tape by reel-to-reel sol-gel dip coating system. Sample were prepared with different wt(1-5)% Ag doped ratio. The surface morphologies and microstructure of all sample were characterized by ESEM, EDS and XRD. Pole figure texture analyses have been done to characterize texture of buffer layer and YBCO superconducting film. The critical current Ic measurement was performed using four wire method with the 1 μV/cm criterion. The critical current density, Jc was measured to be 2.2 × 104 A/cm2 at 77 K self field for 1 wt % Ag doped YBCO sample

AB - Silver doped YBa2Cu3O7-δ (YBCO) coated conductors were fabricated on Gd1.624Ho0.376O 3 (100% lattice match with YBCO) textured buffer layers on Ni tape by reel-to-reel sol-gel dip coating system. Sample were prepared with different wt(1-5)% Ag doped ratio. The surface morphologies and microstructure of all sample were characterized by ESEM, EDS and XRD. Pole figure texture analyses have been done to characterize texture of buffer layer and YBCO superconducting film. The critical current Ic measurement was performed using four wire method with the 1 μV/cm criterion. The critical current density, Jc was measured to be 2.2 × 104 A/cm2 at 77 K self field for 1 wt % Ag doped YBCO sample

KW - Ag doping

KW - Coated conductor

KW - Critical current

KW - Sol-gel

KW - YBCO

UR - https://www.scopus.com/pages/publications/34547430039

U2 - 10.1063/1.2733508

DO - 10.1063/1.2733508

M3 - Conference article

AN - SCOPUS:34547430039

SN - 0094-243X

VL - 899

SP - 767

JO - AIP Conference Proceedings

JF - AIP Conference Proceedings

T2 - 6TH International Conference of the Balkan Physical Union

Y2 - 22 August 2006 through 26 August 2007

ER -

Nonvacuum deposition of silver doped YBCO coated conductor on %100 lattice match buffered Ni tapes

Özet

Belgeye Erişim

Diger dosyalar ve linkler

Parmak izi

Bundan alıntı yap